Demolding challenges in glass-fiber reinforced PA6 injection molding typically arise from:
Improper mold temperature control (too high or too low), causing uneven shrinkage and clamping force.
High residual stress in the part, increasing required ejection force.
Solutions include:
Reducing injection and holding pressure/time
Optimizing melt and mold temperatures
Ensuring adequate draft angles in mold design
Using mold release agents or modifying material formulation