| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 50 mm/min |
66 |
MPa |
ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min |
70 |
MPa |
ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min |
7 |
% |
ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min |
>50 |
% |
ASTM D 638 |
| Tensile Modulus, 5 mm/min |
2100 |
MPa |
ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
95 |
MPa |
ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
2200 |
MPa |
ASTM D 790 |
| Tensile Stress, yield, 50 mm/min |
65 |
MPa |
ISO 527 |
| Tensile Stress, break, 50 mm/min |
60 |
MPa |
ISO 527 |
| Tensile Strain, yield, 50 mm/min |
6 |
% |
ISO 527 |
| Tensile Strain, break, 50 mm/min |
85 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
2150 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
100 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
2300 |
MPa |
ISO 178 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, unnotched, 23°C |
NB |
J/m |
ASTM D 4812 |
| Izod Impact, notched, 23°C |
600 |
J/m |
ASTM D 256 |
| Instrumented Impact Total Energy, 23°C |
120 |
J |
ASTM D 3763 |
| Izod Impact, unnotched 80*10*3 +23°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C |
53 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C |
11 |
kJ/m² |
ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm |
54 |
kJ/m² |
ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm |
13 |
kJ/m² |
ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
| THERMAL |
Value |
Unit |
Standard |
| Vicat Softening Temp, Rate B/50 |
166 |
°C |
ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed |
148 |
°C |
ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed |
142 |
°C |
ASTM D 648 |
| CTE, -40°C to 40°C, flow |
8.E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 40°C, xflow |
8.E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 40°C, flow |
8.E-05 |
1/°C |
ISO 11359-2 |
| CTE, -40°C to 40°C, xflow |
8.E-05 |
1/°C |
ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C |
pass |
- |
IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 |
155 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
157 |
°C |
ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm |
149 |
°C |
ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
137 |
°C |
ISO 75/Ae |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.2 |
- |
ASTM D 792 |
| Mold Shrinkage on Tensile Bar, flow (2) |
0.6 - 0.8 |
% |
S-Plastics Method |
| Mold Shrinkage, flow, 3.2 mm |
0.6 - 0.8 |
% |
S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm |
0 - 0.2 |
% |
S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf |
6 |
g/10 min |
ASTM D 1238 |
| Density |
1.2 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
0.16 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.35 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg |
6 |
cm³/10 min |
ISO 1133 |
| Melt Volume Rate, MVR at 330°C/2.16kg |
29 |
cm³/10 min |
ISO 1133 |
| Source GMD, last updated:11/06/2003 |
|
|