| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 50 mm/min |
62 |
MPa |
ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min |
67 |
MPa |
ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min |
6 |
% |
ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min |
125 |
% |
ASTM D 638 |
| Tensile Modulus, 50 mm/min |
2270 |
MPa |
ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
101 |
MPa |
ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
2150 |
MPa |
ASTM D 790 |
| Tensile Stress, yield, 50 mm/min |
63 |
MPa |
ISO 527 |
| Tensile Stress, break, 50 mm/min |
60 |
MPa |
ISO 527 |
| Tensile Strain, yield, 50 mm/min |
6 |
% |
ISO 527 |
| Tensile Strain, break, 50 mm/min |
110 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
2350 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
90 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
2300 |
MPa |
ISO 178 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, notched, 23°C |
801 |
J/m |
ASTM D 256 |
| Izod Impact, notched, -30°C |
N/A |
J/m |
ASTM D 256 |
| Instrumented Impact Total Energy, 23°C |
79 |
J |
ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C |
60 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C |
12 |
kJ/m² |
ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
N/A |
kJ/m² |
ISO 179/1eA |
| THERMAL |
Value |
Unit |
Standard |
| Vicat Softening Temp, Rate B/50 |
143 |
°C |
ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed |
137 |
°C |
ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed |
126 |
°C |
ASTM D 648 |
| CTE, -40°C to 40°C, flow |
6.84E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 40°C, xflow |
7.38E-05 |
1/°C |
ASTM E 831 |
| CTE, 23°C to 80°C, flow |
7.E-05 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 80°C, xflow |
7.E-05 |
1/°C |
ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 |
144 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
143 |
°C |
ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
130 |
°C |
ISO 75/Ae |
| Relative Temp Index, Elec |
130 |
°C |
UL 746B |
| Relative Temp Index, Mech w/impact |
120 |
°C |
UL 746B |
| Relative Temp Index, Mech w/o impact |
130 |
°C |
UL 746B |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.19 |
- |
ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm |
0.6 - 0.8 |
% |
S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf |
7 |
g/10 min |
ASTM D 1238 |
| Density |
1.2 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
0.35 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.15 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg |
7 |
cm³/10 min |
ISO 1133 |
| ELECTRICAL |
Value |
Unit |
Standard |
| Volume Resistivity |
>1.E+15 |
Ohm-cm |
ASTM D 257 |
| Surface Resistivity |
>1.E+15 |
Ohm |
ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm |
17 |
kV/mm |
ASTM D 149 |
| Relative Permittivity, 50/60 Hz |
2.7 |
- |
ASTM D 150 |
| Relative Permittivity, 1 MHz |
2.7 |
- |
ASTM D 150 |
| Dissipation Factor, 50/60 Hz |
0.001 |
- |
ASTM D 150 |
| Dissipation Factor, 1 MHz |
0.01 |
- |
ASTM D 150 |
| Arc Resistance, Tungsten {PLC} |
7 |
PLC Code |
ASTM D 495 |
| Hot Wire Ignition {PLC) |
1 |
PLC Code |
UL 746A |
| High Voltage Arc Track Rate {PLC} |
2 |
PLC Code |
UL 746A |
| High Ampere Arc Ign, surface {PLC} |
0 |
PLC Code |
UL 746A |
| Comparative Tracking Index (UL) {PLC} |
3 |
PLC Code |
UL 746A |
| FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
| UL Recognized, 94V-2 Flame Class Rating (3) |
0.8 |
mm |
UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) |
3.04 |
mm |
UL 94 |
| Glow Wire Flammability Index 960°C, passes at |
1 |
mm |
IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 1.0 mm |
850 |
°C |
IEC 60695-2-13 |
| Oxygen Index (LOI) |
35 |
% |
ISO 4589 |
| UV-light, water exposure/immersion |
F1 |
- |
UL 746C |
| Source GMD, last updated:07/15/2008 |
|
|