| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 50 mm/min |
57 |
MPa |
ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min |
59 |
MPa |
ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min |
5.6 |
% |
ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min |
123.9 |
% |
ASTM D 638 |
| Tensile Modulus, 50 mm/min |
2180 |
MPa |
ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
92 |
MPa |
ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
2180 |
MPa |
ASTM D 790 |
| Tensile Stress, yield, 50 mm/min |
56 |
MPa |
ISO 527 |
| Tensile Stress, break, 50 mm/min |
55 |
MPa |
ISO 527 |
| Tensile Strain, yield, 50 mm/min |
5.4 |
% |
ISO 527 |
| Tensile Strain, break, 50 mm/min |
108.5 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
2300 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
88 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
2120 |
MPa |
ISO 178 |
| Hardness, Rockwell L |
87 |
- |
ISO 2039-2 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, notched, 23°C |
824 |
J/m |
ASTM D 256 |
| Izod Impact, notched, -30°C |
712 |
J/m |
ASTM D 256 |
| Instrumented Impact Total Energy, 23°C |
75 |
J |
ASTM D 3763 |
| Instrumented Impact Total Energy, -30°C |
77 |
J |
ASTM D 3763 |
| Izod Impact, unnotched 80*10*3 +23°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C |
65 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C |
55 |
kJ/m² |
ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm |
70 |
kJ/m² |
ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm |
60 |
kJ/m² |
ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
| THERMAL |
Value |
Unit |
Standard |
| Vicat Softening Temp, Rate A/50 |
138 |
°C |
ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed |
120 |
°C |
ASTM D 648 |
| CTE, -40°C to 95°C, flow |
6.7E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 95°C, xflow |
8.E-05 |
1/°C |
ASTM E 831 |
| CTE, 23°C to 80°C, flow |
6.7E-05 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 80°C, xflow |
8.E-05 |
1/°C |
ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C |
pass |
- |
IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 |
138 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
139 |
°C |
ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
116 |
°C |
ISO 75/Af |
| Relative Temp Index, Elec |
130 |
°C |
UL 746B |
| Relative Temp Index, Mech w/o impact |
130 |
°C |
UL 746B |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.19 |
- |
ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm |
0.4 - 0.8 |
% |
S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm |
0.4 - 0.8 |
% |
S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf |
10 |
g/10 min |
ASTM D 1238 |
| Density |
1.19 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
0.12 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.09 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg |
9 |
cm³/10 min |
ISO 1133 |
| OPTICAL |
Value |
Unit |
Standard |
| Light Transmission |
82 |
% |
ASTM D 1003 |
| Haze |
3 |
% |
ASTM D 1003 |
| ELECTRICAL |
Value |
Unit |
Standard |
| Volume Resistivity |
>1.E+15 |
Ohm-cm |
ASTM D 257 |
| Surface Resistivity |
>1.E+15 |
Ohm |
ASTM D 257 |
| FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
| UL Recognized, 94V-2 Flame Class Rating (3) |
3 |
mm |
UL 94 |
| Glow Wire Flammability Index 960°C, passes at |
3 |
mm |
IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 0.8 mm |
850 |
°C |
IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm |
850 |
°C |
IEC 60695-2-13 |
| Source GMD, last updated:09/15/2004 |
|
|