| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 50 mm/min |
67 |
MPa |
ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min |
69 |
MPa |
ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min |
6 |
% |
ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min |
107.1 |
% |
ASTM D 638 |
| Tensile Modulus, 50 mm/min |
2580 |
MPa |
ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
108 |
MPa |
ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
2530 |
MPa |
ASTM D 790 |
| Tensile Stress, yield, 50 mm/min |
66 |
MPa |
ISO 527 |
| Tensile Stress, break, 50 mm/min |
67 |
MPa |
ISO 527 |
| Tensile Strain, yield, 50 mm/min |
5.7 |
% |
ISO 527 |
| Tensile Strain, break, 50 mm/min |
111.4 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
2590 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
99 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
2230 |
MPa |
ISO 178 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, unnotched, 23°C |
2607 |
J/m |
ASTM D 4812 |
| Izod Impact, notched, 23°C |
657 |
J/m |
ASTM D 256 |
| Izod Impact, notched, 0°C |
146 |
J/m |
ASTM D 256 |
| Instrumented Impact Total Energy, 23°C |
79 |
J |
ASTM D 3763 |
| Instrumented Impact Total Energy, -20°C |
86 |
J |
ASTM D 3763 |
| Instrumented Impact Total Energy, -40°C |
84 |
J |
ASTM D 3673 |
| Izod Impact, notched 80*10*4 +23°C |
9 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C |
7 |
kJ/m² |
ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
13 |
kJ/m² |
ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm |
6 |
kJ/m² |
ISO 179/1eA |
| THERMAL |
Value |
Unit |
Standard |
| Vicat Softening Temp, Rate B/50 |
135 |
°C |
ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed |
130 |
°C |
ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed |
120 |
°C |
ASTM D 648 |
| CTE, -40°C to 40°C, flow |
6.66E-05 |
1/°C |
ISO 11359-2 |
| CTE, -40°C to 40°C, xflow |
6.48E-05 |
1/°C |
ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C |
PASSES |
- |
IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 |
134 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
137 |
°C |
ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
129 |
°C |
ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
117 |
°C |
ISO 75/Af |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.22 |
- |
ASTM D 792 |
| Water Absorption, 24 hours |
0.115 |
% |
ASTM D 570 |
| Mold Shrinkage on Tensile Bar, flow (2) |
0.5 - 0.7 |
% |
S-Plastics Method |
| Mold Shrinkage, flow, 3.2 mm |
0.5 - 0.7 |
% |
S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm |
0.5 - 0.7 |
% |
S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf |
10 |
g/10 min |
ASTM D 1238 |
| Density |
1.22 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
0.24 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.17 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg |
9 |
cm³/10 min |
ISO 1133 |
| OPTICAL |
Value |
Unit |
Standard |
| Light Transmission |
84 |
% |
ASTM D 1003 |
| Haze |
0.8 |
% |
ASTM D 1003 |
| Refractive Index |
1.59 |
- |
ASTM D 542 |
| Yellowness Index |
0 |
- |
ASTM D 1925 |
| Source GMD, last updated:02/15/2005 |
|
|