| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 50 mm/min |
51 |
MPa |
ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min |
200 |
% |
ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
82 |
MPa |
ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
2340 |
MPa |
ASTM D 790 |
| Hardness, Rockwell R |
117 |
- |
ASTM D 785 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, unnotched, 23°C |
1602 |
J/m |
ASTM D 4812 |
| Izod Impact, notched, 23°C |
53 |
J/m |
ASTM D 256 |
| Modified Gardner, 23°C |
40 |
J |
ASTM D 3029 |
| THERMAL |
Value |
Unit |
Standard |
| HDT, 0.45 MPa, 6.4 mm, unannealed |
154 |
°C |
ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed |
54 |
°C |
ASTM D 648 |
| CTE, -40°C to 40°C, flow |
8.1E-05 |
1/°C |
ASTM E 831 |
| CTE, 60°C to 138°C, flow |
1.39E-04 |
1/°C |
ASTM E 831 |
| Relative Temp Index, Elec |
120 |
°C |
UL 746B |
| Relative Temp Index, Mech w/impact |
120 |
°C |
UL 746B |
| Relative Temp Index, Mech w/o impact |
140 |
°C |
UL 746B |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.31 |
- |
ASTM D 792 |
| Specific Volume |
0.76 |
cm³/g |
ASTM D 792 |
| Water Absorption, 24 hours |
0.08 |
% |
ASTM D 570 |
| Water Absorption, equilibrium, 23C |
0.34 |
% |
ASTM D 570 |
| Mold Shrinkage, flow, 0.75-2.3 mm |
0.9 - 1.6 |
% |
S-Plastics Method |
| Mold Shrinkage, flow, 2.3-4.6 mm |
1.5 - 2.3 |
% |
S-Plastics Method |
| Mold Shrinkage, xflow, 0.75-2.3 mm |
1 - 1.7 |
% |
S-Plastics Method |
| Mold Shrinkage, xflow, 2.3-4.6 mm |
1.6 - 2.4 |
% |
S-Plastics Method |
| ELECTRICAL |
Value |
Unit |
Standard |
| Volume Resistivity |
>4.E+16 |
Ohm-cm |
ASTM D 257 |
| Dielectric Strength, in air, 3.2 mm |
15.7 |
kV/mm |
ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm |
23.2 |
kV/mm |
ASTM D 149 |
| Dielectric Strength, in oil, 3.2 mm |
15.7 |
kV/mm |
ASTM D 149 |
| Relative Permittivity, 100 Hz |
3.3 |
- |
ASTM D 150 |
| Relative Permittivity, 1 MHz |
3.1 |
- |
ASTM D 150 |
| Dissipation Factor, 100 Hz |
0.002 |
- |
ASTM D 150 |
| Dissipation Factor, 1 MHz |
0.02 |
- |
ASTM D 150 |
| Arc Resistance, Tungsten {PLC} |
4 |
PLC Code |
ASTM D 495 |
| Hot Wire Ignition {PLC) |
3 |
PLC Code |
UL 746A |
| High Voltage Arc Track Rate {PLC} |
1 |
PLC Code |
UL 746A |
| High Ampere Arc Ign, surface {PLC} |
0 |
PLC Code |
UL 746A |
| Comparative Tracking Index (UL) {PLC} |
0 |
PLC Code |
UL 746A |
| FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
| UL Recognized, 94HB Flame Class Rating (3) |
0.83 |
mm |
UL 94 |
| UV-light, water exposure/immersion |
F1 |
- |
UL 746C |
| Source GMD, last updated:01/05/2000 |
|
|