| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, break, 5 mm/min |
110 |
MPa |
ISO 527 |
| Tensile Strain, break, 5 mm/min |
2.5 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
7000 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
165 |
MPa |
ISO 178 |
| Flexural Stress, break, 2 mm/min |
145 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
6000 |
MPa |
ISO 178 |
| Hardness, H358/30 |
119 |
MPa |
ISO 2039-1 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, unnotched 80*10*4 +23°C |
40 |
kJ/m² |
ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C |
35 |
kJ/m² |
ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C |
7 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C |
6 |
kJ/m² |
ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
6 |
kJ/m² |
ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm |
5 |
kJ/m² |
ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm |
40 |
kJ/m² |
ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm |
40 |
kJ/m² |
ISO 179/1eU |
| THERMAL |
Value |
Unit |
Standard |
| CTE, 23°C to 60°C, flow |
4.E-05 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 60°C, xflow |
1.E-04 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 80°C, flow |
4.E-05 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 80°C, xflow |
1.E-04 |
1/°C |
ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C |
PASSES |
- |
IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 |
212 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/50 |
140 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
144 |
°C |
ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm |
155 |
°C |
ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
115 |
°C |
ISO 75/Ae |
| PHYSICAL |
Value |
Unit |
Standard |
| Mold Shrinkage on Tensile Bar, flow (2) |
0.3 - 0.8 |
% |
S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) |
0.5 - 0.9 |
% |
S-Plastics Method |
| Density |
1.39 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
0.1 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.06 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg |
13 |
cm³/10 min |
ISO 1133 |
| ELECTRICAL |
Value |
Unit |
Standard |
| Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
| Surface Resistivity, ROA |
>1.E+15 |
Ohm |
IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm |
31 |
kV/mm |
IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm |
24 |
kV/mm |
IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm |
16 |
kV/mm |
IEC 60243-1 |
| Relative Permittivity, 50/60 Hz |
3.1 |
- |
IEC 60250 |
| Relative Permittivity, 100 Hz |
3.3 |
- |
IEC 60250 |
| Relative Permittivity, 1 MHz |
3 |
- |
IEC 60250 |
| Dissipation Factor, 50/60 Hz |
0.001 |
- |
IEC 60250 |
| Dissipation Factor, 100 Hz |
0.001 |
- |
IEC 60250 |
| Dissipation Factor, 1 MHz |
0.011 |
- |
IEC 60250 |
| Comparative Tracking Index |
200 |
V |
IEC 60112 |
| Comparative Tracking Index, M |
100 |
V |
IEC 60112 |
| FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) |
1.6 |
mm |
UL 94 by GE |
| Glow Wire Flammability Index 750°C, passes at |
1 |
mm |
IEC 60695-2-12 |
| Glow Wire Flammability Index 850°C, passes at |
2 |
mm |
IEC 60695-2-12 |
| Oxygen Index (LOI) |
23 |
% |
ISO 4589 |
| Source GMD, last updated:10/05/2000 |
|
|