| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 5 mm/min |
110 |
MPa |
ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min |
105 |
MPa |
ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min |
7 |
% |
ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min |
60 |
% |
ASTM D 638 |
| Tensile Modulus, 5 mm/min |
3590 |
MPa |
ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
165 |
MPa |
ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
3520 |
MPa |
ASTM D 790 |
| Tensile Stress, yield, 5 mm/min |
105 |
MPa |
ISO 527 |
| Tensile Stress, break, 5 mm/min |
85 |
MPa |
ISO 527 |
| Tensile Strain, yield, 5 mm/min |
6 |
% |
ISO 527 |
| Tensile Strain, break, 5 mm/min |
60 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
3200 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
160 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
3300 |
MPa |
ISO 178 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, unnotched, 23°C |
1335 |
J/m |
ASTM D 4812 |
| Izod Impact, notched, 23°C |
32 |
J/m |
ASTM D 256 |
| Izod Impact, notched, -30°C |
35 |
J/m |
ASTM D 256 |
| Instrumented Impact Total Energy, 23°C |
33 |
J |
ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C |
5 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C |
5 |
kJ/m² |
ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
3 |
kJ/m² |
ISO 179/1eA |
| THERMAL |
Value |
Unit |
Standard |
| Vicat Softening Temp, Rate B/50 |
219 |
°C |
ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed |
205 |
°C |
ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed |
197 |
°C |
ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed |
199 |
°C |
ASTM D 648 |
| CTE, -40°C to 150°C, flow |
5.5E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 150°C, xflow |
5.5E-05 |
1/°C |
ASTM E 831 |
| CTE, 23°C to 150°C, flow |
5.E-05 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 150°C, xflow |
5.E-05 |
1/°C |
ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 |
211 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
212 |
°C |
ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
190 |
°C |
ISO 75/Ae |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
193 |
°C |
ISO 75/Af |
| Metallized Haze Onset |
204 |
°C |
S-Plastics Method |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.27 |
- |
ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm |
0.5 - 0.7 |
% |
S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf |
17.8 |
g/10 min |
ASTM D 1238 |
| Density |
1.27 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
1.25 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.7 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg |
25 |
cm³/10 min |
ISO 1133 |
| Source GMD, last updated:11/09/2007 |
|
|