| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 50 mm/min |
58 |
MPa |
ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min |
5 |
% |
ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min |
50 |
% |
ASTM D 638 |
| Tensile Modulus, 50 mm/min |
2680 |
MPa |
ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span |
96 |
MPa |
ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span |
2680 |
MPa |
ASTM D 790 |
| Hardness, Rockwell R |
120 |
- |
ASTM D 785 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, notched, 23°C |
427 |
J/m |
ASTM D 256 |
| Instrumented Impact Total Energy, 23°C |
58 |
J |
ASTM D 3763 |
| THERMAL |
Value |
Unit |
Standard |
| Vicat Softening Temp, Rate B/50 |
90 |
°C |
ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed |
73 |
°C |
ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed |
80 |
°C |
ASTM D 648 |
| CTE, -40°C to 60°C, flow |
8.1E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 60°C, xflow |
8.1E-05 |
1/°C |
ASTM E 831 |
| Thermal Conductivity |
0.2 |
W/m-°C |
ASTM C 177 |
| Relative Temp Index, Elec |
80 |
°C |
UL 746B |
| Relative Temp Index, Mech w/impact |
70 |
°C |
UL 746B |
| Relative Temp Index, Mech w/o impact |
80 |
°C |
UL 746B |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.17 |
- |
ASTM D 792 |
| Specific Gravity, color |
1.18 |
- |
ASTM D 792 |
| Water Absorption, 24 hours |
0.2 |
% |
ASTM D 570 |
| Water Absorption, equilibrium, 23C |
0.6 |
% |
ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm |
0.4 - 0.6 |
% |
S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm |
0.4 - 0.6 |
% |
S-Plastics Method |
| Melt Flow Rate, 260°C/2.16 kgf |
16 |
g/10 min |
ASTM D 1238 |
| ELECTRICAL |
Value |
Unit |
Standard |
| Volume Resistivity |
1.E+17 |
Ohm-cm |
ASTM D 257 |
| Surface Resistivity |
>1.E+14 |
Ohm |
ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm |
17.9 |
kV/mm |
ASTM D 149 |
| Relative Permittivity, 50/60 Hz |
3 |
- |
ASTM D 150 |
| Relative Permittivity, 100 Hz |
3 |
- |
ASTM D 150 |
| Dissipation Factor, 50/60 Hz |
0.0048 |
- |
ASTM D 150 |
| Arc Resistance, Tungsten {PLC} |
6 |
PLC Code |
ASTM D 495 |
| Hot Wire Ignition {PLC) |
3 |
PLC Code |
UL 746A |
| High Voltage Arc Track Rate {PLC} |
3 |
PLC Code |
UL 746A |
| High Ampere Arc Ign, surface {PLC} |
0 |
PLC Code |
UL 746A |
| Comparative Tracking Index (UL) {PLC} |
1 |
PLC Code |
UL 746A |
| FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
| UL Recognized, 94V-2 Flame Class Rating (3) |
0.88 |
mm |
UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) |
1.49 |
mm |
UL 94 |
| UL Recognized, 94-5VB Rating (3) |
2.31 |
mm |
UL 94 |
| CSA (See File for complete listing) |
LS88480 |
File No. |
CSA LISTED |
| Oxygen Index (LOI) |
35 |
% |
ASTM D 2863 |
| Source GMD, last updated:01/05/2000 |
|
|