| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 50 mm/min |
50 |
MPa |
ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min |
52 |
MPa |
ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min |
5 |
% |
ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min |
150 |
% |
ASTM D 638 |
| Tensile Modulus, 5 mm/min |
2100 |
MPa |
ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
70 |
MPa |
ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
2000 |
MPa |
ASTM D 790 |
| Tensile Stress, yield, 50 mm/min |
50 |
MPa |
ISO 527 |
| Tensile Stress, break, 50 mm/min |
55 |
MPa |
ISO 527 |
| Tensile Strain, yield, 50 mm/min |
5 |
% |
ISO 527 |
| Tensile Strain, break, 50 mm/min |
100 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
2050 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
75 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
2050 |
MPa |
ISO 178 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, notched, 23°C |
750 |
J/m |
ASTM D 256 |
| Izod Impact, notched, -30°C |
600 |
J/m |
ASTM D 256 |
| Instrumented Impact Total Energy, 23°C |
80 |
J |
ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 -40°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C |
55 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C |
25 |
kJ/m² |
ISO 180/1A |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
60 |
kJ/m² |
ISO 179/1eA |
| THERMAL |
Value |
Unit |
Standard |
| Vicat Softening Temp, Rate B/50 |
125 |
°C |
ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed |
80 |
°C |
ASTM D 648 |
| CTE, -40°C to 40°C, flow |
9.E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 40°C, xflow |
9.E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 40°C, flow |
9.E-05 |
1/°C |
ISO 11359-2 |
| CTE, -40°C to 40°C, xflow |
9.E-05 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 60°C, flow |
1.E-04 |
1/°C |
ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 |
125 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
123 |
°C |
ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
105 |
°C |
ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
80 |
°C |
ISO 75/Af |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.22 |
- |
ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm |
0.7 - 1.1 |
% |
S-Plastics Method |
| Melt Flow Rate, 250°C/5.0 kgf |
11 |
g/10 min |
ASTM D 1238 |
| Density |
1.22 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
0.4 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.05 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 250°C/5.0 kg |
10 |
cm³/10 min |
ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 |
260 |
Pa-s |
ISO 11443 |
| Source GMD, last updated:03/14/2008 |
|
|