| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Tensile Stress, yld, Type I, 50 mm/min |
46 |
MPa |
ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min |
34 |
MPa |
ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min |
2.7 |
% |
ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min |
11 |
% |
ASTM D 638 |
| Tensile Modulus, 5 mm/min |
2220 |
MPa |
ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
64 |
MPa |
ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
2070 |
MPa |
ASTM D 790 |
| Tensile Stress, yield, 50 mm/min |
44 |
MPa |
ISO 527 |
| Tensile Stress, break, 50 mm/min |
36 |
MPa |
ISO 527 |
| Tensile Strain, yield, 50 mm/min |
2.6 |
% |
ISO 527 |
| Tensile Strain, break, 50 mm/min |
5 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
2150 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
62 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
2100 |
MPa |
ISO 178 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, notched, 23°C |
70 |
J/m |
ASTM D 256 |
| Izod Impact, notched, -30°C |
20 |
J/m |
ASTM D 256 |
| Instrumented Impact Total Energy, 23°C |
7 |
J |
ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C |
7 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C |
3 |
kJ/m² |
ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
8 |
kJ/m² |
ISO 179/1eA |
| THERMAL |
Value |
Unit |
Standard |
| Vicat Softening Temp, Rate B/50 |
85 |
°C |
ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed |
76 |
°C |
ASTM D 648 |
| CTE, -40°C to 60°C, flow |
9.8E-05 |
1/°C |
ASTM E 831 |
| CTE, -40°C to 60°C, xflow |
9.8E-05 |
1/°C |
ASTM E 831 |
| CTE, 23°C to 60°C, flow |
9.7E-05 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 60°C, xflow |
9.9E-05 |
1/°C |
ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 |
102 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/50 |
89 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
90 |
°C |
ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
86 |
°C |
ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
77 |
°C |
ISO 75/Af |
| PHYSICAL |
Value |
Unit |
Standard |
| Specific Gravity |
1.2 |
- |
ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm |
0.4 - 0.7 |
% |
S-Plastics Method |
| Melt Flow Rate, 220°C/10.0 kgf |
30 |
g/10 min |
ASTM D 1238 |
| Density |
1.2 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
0.45 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.16 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 220°C/10.0 kg |
27 |
cm³/10 min |
ISO 1133 |
| ELECTRICAL |
Value |
Unit |
Standard |
| Dielectric Strength, in oil, 0.8 mm |
41 |
kV/mm |
ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm |
24 |
kV/mm |
ASTM D 149 |
| Dielectric Strength, in oil, 3.2 mm |
18 |
kV/mm |
ASTM D 149 |
| Relative Permittivity, 1 kHz |
3.4 |
- |
ASTM D 150 |
| Relative Permittivity, 1 MHz |
3.2 |
- |
ASTM D 150 |
| Dissipation Factor, 1 kHz |
0.008 |
- |
ASTM D 150 |
| Dissipation Factor, 1 MHz |
0.029 |
- |
ASTM D 150 |
| Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
| Surface Resistivity, ROA |
>1.E+16 |
Ohm |
IEC 60093 |
| Comparative Tracking Index, M |
600 |
V |
IEC 60112 |
| FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) |
1.5 |
mm |
UL 94 |
| UL Recognized, 94-5VA Rating (3) |
3 |
mm |
UL 94 |
| UL Recognized, 94-5VB Rating (3) |
1.5 |
mm |
UL 94 |
| Glow Wire Flammability Index 960°C, passes at |
2 |
mm |
IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 1.0 mm |
750 |
°C |
IEC 60695-2-13 |
| Oxygen Index (LOI) |
25 |
% |
ISO 4589 |
| Source GMD, last updated:01/08/2007 |
|
|