| TYPICAL PROPERTIES (1) |
|
|
|
| MECHANICAL |
Value |
Unit |
Standard |
| Taber Abrasion, CS-17, 1 kg |
15 |
mg/1000cy |
S-Plastics Method |
| Tensile Stress, break, 5 mm/min |
115 |
MPa |
ISO 527 |
| Tensile Strain, break, 5 mm/min |
4 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
4500 |
MPa |
ISO 527 |
| Flexural Stress, break, 2 mm/min |
185 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
4500 |
MPa |
ISO 178 |
| Hardness, H358/30 |
140 |
MPa |
ISO 2039-1 |
| IMPACT |
Value |
Unit |
Standard |
| Izod Impact, unnotched 80*10*4 +23°C |
30 |
kJ/m² |
ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C |
30 |
kJ/m² |
ISO 180/1U |
| Charpy Impact, notched, 23°C |
7 |
kJ/m² |
ISO 179/2C |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm |
35 |
kJ/m² |
ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm |
35 |
kJ/m² |
ISO 179/1eU |
| THERMAL |
Value |
Unit |
Standard |
| Thermal Conductivity |
0.24 |
W/m-°C |
ISO 8302 |
| CTE, 23°C to 150°C, flow |
2.6E-05 |
1/°C |
ISO 11359-2 |
| CTE, 23°C to 150°C, xflow |
6.E-05 |
1/°C |
ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C |
PASSES |
- |
IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 |
223 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/50 |
212 |
°C |
ISO 306 |
| Vicat Softening Temp, Rate B/120 |
217 |
°C |
ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm |
210 |
°C |
ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
205 |
°C |
ISO 75/Ae |
| PHYSICAL |
Value |
Unit |
Standard |
| Mold Shrinkage on Tensile Bar, flow (2) |
0.4 - 0.6 |
% |
S-Plastics Method |
| Density |
1.34 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/sat) |
1 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.6 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg |
13 |
cm³/10 min |
ISO 1133 |
| ELECTRICAL |
Value |
Unit |
Standard |
| Volume Resistivity |
1.E+15 |
Ohm-cm |
IEC 60093 |
| Surface Resistivity, ROA |
>1.E+15 |
Ohm |
IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm |
34 |
kV/mm |
IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm |
27 |
kV/mm |
IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm |
15 |
kV/mm |
IEC 60243-1 |
| Relative Permittivity, 50/60 Hz |
3 |
- |
IEC 60250 |
| Relative Permittivity, 1 MHz |
2.9 |
- |
IEC 60250 |
| Dissipation Factor, 50/60 Hz |
0.0009 |
- |
IEC 60250 |
| Dissipation Factor, 1 MHz |
0.0025 |
- |
IEC 60250 |
| Dissipation Factor, 2450 MHz |
0.0046 |
- |
IEC 60250 |
| Comparative Tracking Index |
150 |
V |
IEC 60112 |
| Comparative Tracking Index, M |
100 |
V |
IEC 60112 |
| FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
| Glow Wire Flammability Index 960°C, passes at |
3.2 |
mm |
IEC 60695-2-12 |
| Oxygen Index (LOI) |
46 |
% |
ISO 4589 |
| Source GMD, last updated:10/11/2006 |
|
|